One-step Cathodic Electrochemical Synthesis and Characterization of Dextran Coated Magnetite Nanoparticles

Journal of Nanoanalysis

مقاله 7، دوره 4، شماره 3، آذر 2017، صفحه 228-238   

نوع مقاله: Original Research Paper

شناسه دیجیتال (DOI): 10.22034/jna.2017.539366

نویسندگان

Mustafa Aghazadeh^{* 1}؛ Isa Karimzadeh²

¹Materials and Nuclear Research School, Nuclear Science and Technology Research Institute (NSTRI), P.O. Box 14395-834, Tehran, Iran

²Department of Physics, Faculty of Science, Central Tehran Branch, Islamic Azad University, Tehran, Iran

چکیده

In this research, a simple and efficient cathodic electrochemical deposition (CED) route was
developed for the preparation of magnetite nanoparticles (NPs) in an aqueous media. The
surface of magnetite NPs was also coated for the first time via an in situ procedure during the
CED process. In this method, initially, the Fe3O4 NPs (with size ~10 nm) were prepared from the
Fe2+/Fe3+ chloride bath through CED process. Then, dextran as the coating agent was coated
on the surface of Fe3O4 NPs during the CED process. The prepared NPs were characterized
by different techniques such as XRD, FE-SEM, TEM, IR, TGA, DLS and VSM. The XRD results
proved the pure magnetite i.e. Fe3O4 crystal phase of the prepared samples. Morphological
observations through FE-SEM and TEM revealed particle morphology with nano-sizes of 8
nm and 12 nm for the naked and dextran coated NPs, respectively. The dextran coat on the
surfaces of NPs was confirmed by FT-IR and DSC-TGA analyses. The average hydrodynamic
diameters of 17 nm and 54 nm were measured from DLS analysis for the naked and dextran
coated NPs, respectively. The magnetic analysis by VSM revealed that prepared NPs have
superparamagnetic behavior, i.e. Ms=82.3 emu g–1, magnetization Mr=0.71 emug–1 and Ce=2.3
Oe for the naked NPs, and Ms=43.1 emu g–1, Mr=0.47 emu g–1 and Ce=0.81Oe for the dextran
coated NPs. These results implied that this electrochemical strategy can be recognized as an
effective preparation method of polymer coated Fe3O4 NPs.

کلیدواژه‌ها

Magnetite؛ nanoparticles؛ Cathodic Electrodeposition؛ In situ coating؛ Dextran