Optical and photocatalytic properties Undoped and Mn-doped ZnO nanoparticles synthesized by hydrothermal method: Effect of annealing temperature

Iranian Journal of Catalysis

مقاله 6، دوره 5، شماره 2، شهریور 2015، صفحه 135-141   

نوع مقاله: Articles

نویسندگان

Maryam Bordbar^{* 1}؛ Seyed Mohammad Vasegh²؛ Somaye Jafari³؛ Ali Yeganeh Faal³

¹Department of Chemistry, Faculty of Science, University of Qom, Qom, Iran.

²Faculty of Technical & Engineering, Islamic Azad University, Tehran South Branch, Tehran, Iran.

³Faculty of Science, Payame Noor University, Qom, Iran.

چکیده

Undoped and Mn-doped ZnO nanoparticles were successfully prepared by the hydrothermal method with different annealing temperature conditions. Structural, chemical and optical properties of the samples were studied by X-ray diffraction (XRD), Field Emission scanning electron microscopy (FESEM), UV-Vis spectrophotometry and Fourier transform infrared (FT-IR) spectroscopy. The phase purity was confirmed by X-ray powder diffraction (XRD) and XRD spectra showed that all the samples were hexagonal wurtzite structure and as the annealing temperature increases the material becomes less crystalline. In addition, the average crystal size was found to be 15-30 nm from SEM and XRD. It is seen that the optical band gap increases when the ZnO is doped with manganese and decreases when annealing temperature increases. The photoacatalytic activity of Undoped and Mn-doped ZnO nanoparticles was tested by the degradation of metyl orang (MO) under UV light and indicated that Mn-doped ZnO has higher photocatalytic activity relative to ZnO nanoparticles and photocatalytic activity decreases when annealing temperature increases.

کلیدواژه‌ها

Mn-doped ZnO؛ photocatalyst؛ Hydrothermal method؛ Annealing temperature

مراجع

[1] A. Umar, Y.B. Hahn, Metal oxide nanostructures and their applications, American Scientific Publication, 2010.
[2] O.I. Lupan, S.T. Shishiyanu, T.S. Shishiyanu, Superlattices Microstruct. 42 (2007) 375-378.
[3] J. Guo, J. Zhang, M. Zhu, D. Ju, H. Xu, B. Cao, Sens. Actuators B: Chem. 199 (2014) 339-345.
[4] R. Khan, M.S. Hassan, L.W. Jang, J.H. Yun, H.K. Ahn, M.S. Khil, I.H. Lee, Ceram. Int. 40 (2014) 14827-14831.
[5] Y. Chen, D. Bagnall, T. Yao, Mater. Sci. Eng. B 75 (2000) 190-198.
[6] E.R. Carraway, A.J. Hoffman, M.R. Hoffmann, Environ. Sci. Technol. 28 (1994) 786-793.
[7] I. Poulios, D. Makri, X. Prohaska, Global Nest: Int. J. 1 (1999) 55-62.
[8] B. Pal, M. Sharon, Mater. Chem. Phys. 76 (2002) 82-87.
[9] R.Y. Hong, S.Z. Zhang, G.Q. Di, H.Z. Li, Y. Zheng, J. Ding, D.G. Wei, Mater. Res. Bull. 43 (2008) 2457-2468.
[10] C. Xu, L. Cao, G. Su, W. Liu, X. Qu, Y. Yu, J. Alloys Compd. 497 (2010) 373-376.
[11] C. Wu, L. Shen, H. Yu, Q. Huang, Y.C. Zhang, Mater. Res. Bull. 46 (2011) 1107-1112.
[12] S. Yılmaz, E. McGlynn, E. Bacaksız, J. Cullen, R.K. Chellappan, Chem. Phys. Lett. 525–526 (2012) 72-76.
[13] R. Ullah, J. Dutta, J. Hazard. Mater. 156 (2008) 194-200.
[14] M.A. Mahmood, S. Baruah, J. Dutta, Mater. Chem. Phys. 130 (2011) 531-535.
[15] X. Zhang, J. Qin, Y. Xue, P. Yu, B. Zhang, L. Wang, R. Liu, Sci. Rep. 4 (2014).
[16] Y.L. Chen, C.E. Zhang, C. Deng, P. Fei, M. Zhong, B.T. Su, Chin. Chem. Lett. 24 (2013) 518-520.
[17] L. Shi, L. Liang, J. Ma, J. Sun, Superlattices Microstruct. 62 (2013) 128-139.
[18] J.B. Zhong, J.Z. Li, X.Y. He, J. Zeng, Y. Lu, W. Hu, K. Lin, Curr. Appl. Phys. 12 (2012) 998-1001.
[19] M. Ahmad, E. Ahmed, Z.L. Hong, X.L. Jiao, T. Abbas, N.R. Khalid, Appl. Surf. Sci. B. 285 (2013) 702-712.
[20] J.C. Sin, S.-M. Lam, I. Satoshi, K.T. Lee, A.R. Mohamed, Appl. Catal. B: Environ. 148–149 (2014) 258-268.
[21] H. Wang, C. Xie, J. Phys. Chem. Solids 69 (2008) 2440–2444.
[22] K. Omri, J. El Ghoul, O.M. Lemine, M. Bououdina, B. Zhang, L. El Mir, Superlattices Microstruct. 60 (2013) 139-147.
[23] A. Patterson, Phys. Rev. 56 (1939) 978.
[24] R. Saravanan, V.K. Gupta, V. Narayanan, A. Stephen, J. Mol. Liq. 181 (2013) 133-141.
[25] K. Kaviyarasu, P.A. Devarajan, Adv.Mat. Lett. 4 (2013) 582-585.
[26] S. Senthilkumaar, K. Rajendran, S. Banerjee, T.K. Chini, V. Sengodan, Mater. Sci. Semicond. Process 11 (2008) 6-12.
[27] L. Brus, J. Phys. Chem. 90 (1986) 2555-2560.
[28] Y.S. Wang, P.J. Thomas, P. O'Brien, J. Phys. Chem. B. 110 (2006) 21412-21415.
[29] Z. Banu Bahşi, A.Y. Oral, Opt. Mater. 29 (2007) 672-678.
[30] N.S. Sabri, A.K. Yahya, M.K. Talari, J. Lumin. 132 (2012) 1735-1739.
[31] M. Wen, M. Cheng, S. Zhou, Q. Wu, N. Wang, L. Zhou, J. Phys. Chem. C. 116 (2012) 11702-11708.
[32] S. Yamamoto, H. Watarai, J. Phys. Chem. C. 112 (2008) 12417-12424.