Photodegradation of reactive red 222 using TiO2 nanostructured thin films prepared by modified sol-gel method

International Journal of Nano Dimension

مقاله 10، دوره 5، Issue 5، بهمن 2014، صفحه 489-495   

نوع مقاله: Reasearch Paper

شناسه دیجیتال (DOI): 10.7508/ijnd.2014.05.009

نویسندگان

F. Oshani¹؛ S. Rasouli^{* 2}؛ R. Marandi¹؛ M. Keramati Farhoud²

¹Department of Engineering, Islamic Azad University, North Branch, Tehran, Iran.

²Department of Nanomaterials and Nanotechnology, Institute for Color Science and Technology.

چکیده

In this paper, a modified sol-gel method using peroxotitanic acid sol (PTA) was applied for the preparation of TiO₂ nanostructured thin films on glass plates. The peroxotitanic acid sol was synthesized using titanium isopropoxide, isopropylalchol, H₂O and hydrogen peroxide. TiO₂ films were then calcined at 500^oC and characterized by X-ray diffraction (XRD) and scanning electron microscopy (SEM). XRD results showed that increasing the number of coated layers would lead to the formation of anatase phase at high level. Addition of Polyethylene Glycol (PEG) on the PTA sol could cause uniform coating without any cracks. The photocatalytic performance of the obtained films was investigated by the photodegradation measurements of Reactive Red 222 (RR222) in a batch reactor. For further investigations the effect of some parameters such as initial RR222 concentration, pH value, hydrogen peroxide addition and temperature on the photocatalytic performance of TiO₂ thin films was studies as the important factors. Kinetic study results of this reaction represented that it obeys of was pseudo-first-order model. The degradation of RR22 was enhanced by the addition of optimum amount of hydrogen peroxide. This is due to the increasing amount of the radical hydroxyls.

کلیدواژه‌ها

Modified sol-gel؛ photocatalyst؛ PTA؛ TiO2؛ RR222