EPR studies of Cd substituted Mn Zn nanoferrites

International Journal of Nano Dimension

مقاله 5، دوره 6، شماره 3، مهر 2015، صفحه 255-261   

نوع مقاله: Reasearch Paper

شناسه دیجیتال (DOI): 10.7508/ijnd.2015.03.004

نویسندگان

C. Venkataraju^* ؛ R. Paulsingh

Department of Physics, Karpaga Vinayaga College of Engineering and Technology, Near Madhuranthagam, 603 308, India.

چکیده

Nanoparticles of Mn_0.5Zn_0.5-xCd_xFe₂O₄ with x varying from x = 0.0 to 0.3 were prepared by wet chemical co-precipitation method. The structural and magnetic properties were studied by using X-Ray Diffraction (XRD), Scanning Electron Microscope (SEM), Transmission Electron Microscopy (TEM) and Electron Paramagnetic Resonance (EPR) technique. The lattice constant increases with increase in Cd content. This increase in the lattice constant is due to larger ionic radii of the Cd²⁺ (0.97 Å) ions as compared to Fe³⁺ (0.64 Å) ions. The intensities of the planes (220) and (440), increases with increasing Cd²⁺ ion concentration. This shows that Cd²⁺ ions occupy tetrahedral A sites and octahedral B sites in the nano dimension against their chemical preference for A site. The line width (ΔH_pp) and the g value of the Electron paramagnetic resonance (EPR) signal decreases with increase in the Cd content. The magnetic moment of all the samples up to x = 0.2 calculated from EPR studies are lower when compared to the theoretical values. This lower value of magnetic moment confirms the existence of non collinear magnetic structure arising due to significant amount of spin disorder existing at B site.

کلیدواژه‌ها

Nanostructured materials؛ Chemical synthesis؛ Electron paramagnetic resonance (EPR)؛ Magnetic property؛ Scanning Electron Microscope (SEM)