Structural, magnetic and electrical properties of pure and Dy-doped Fe2O3 nanostructures synthesized using chemical thermal decomposition technique

International Journal of Nano Dimension

مقاله 8، دوره 9، شماره 2، تیر 2018، صفحه 179-190   

نوع مقاله: Reasearch Paper

نویسندگان

Mahbobeh Jafari؛ Mahdi Salehi^* ؛ Mahdi Behzad

Department of Chemistry, Semnan University, Semnan, Iran.

چکیده

Pure (S₁) and Dy³⁺-doped α-Fe₂O₃ (S₂ and S₃) nanoparticles were prepared by a combustion synthesis method at 700 ºC for 8 h using Fe(acac)₃ (Tris(acetylacetonato)Iron(III)) as raw material. Characterizations of the prepared powders were carried out by powder X-ray diffraction (PXRD). Structural analysis was performed by the FullProf program employing profile matching with constant scale factors. Scanning electron microscopy (SEM), transmission electron microscopy (TEM), electrochemical impedance spectroscopy (EIS), elemental maps analysis and energy-dispersive X-ray spectroscopy (EDS) were also performed to determine the dopant amount in the α-Fe₂O₃ crystal structure (S₃). The results showed that the patterns had a main hexagonal structure with space group R . The cell parameters data, calculated by rietveld analysis, showed that the cell parameters were decreased with increasing the dopant (Dy³⁺) amount in the α-Fe₂O₃ crystal structure. The average particles sizes estimated from TEM images for S₃ were about 60 nm. Besides, the magnetic properties of S₁ and S₃ were measured by vibrating sample magnetometer (VSM). It was found that with the addition of Dy³⁺ ions into the Fe₂O₃ system, the coercivity was decreased and the remanent magnetization was abruptly increased. The influence of dysprosium addition was also studied using electrochemical impedance spectroscopy. This study showed that in the presence of dysprosium ion, the charge transfer resistant increased in the electrochemical process.

کلیدواژه‌ها

Combustion synthesis؛ electrochemical impedance spectroscopy؛ Magnetic property؛ Nano-structure characterization؛ X-ray powder diffraction

مراجع

[1] Xinghong W., Li Z., Yonghong N., Jianming H., Xiaofeng C., (2009), Fast preparation, characterization, and property study of α-Fe₂O₃ nanoparticles via a simple solution combusting method. J. Phys. Chem. 113: 7003-7008.

[2] Kesavan V., Sivanand P. S., Chandrasekaran S., Koltypin Yu., Gedanken A., (1999), Catalytic aerobic oxidation of cycloalkanes with nanostructured amorphous metals and alloys. Angew. Chem. Int. Ed. 38: 3521-3523.

[3] Huo L. H., Li W., Lu  L. H., Cui H. N., Xi S. Q., Wang J., Zhao B., Shen Y. C., Lu Z. H., (2000), Preparation, structure, and properties of three-dimensional ordered α-Fe₂O₃ nanoparticulate film. Chem. Mater. 12: 790-794.

[4] Suresh K., Patil K. C., (1993), A combustion process for the instant synthesis of γ-iron oxide. J. Mater. Sci. Lett. 12: 572-574.

[5] Kroell M., Pridoehl M., Zimmermann G., Pop L., Odenbach S., Hartwig A., Magn J., (2005), Magnetic and rheological characterization of novel ferrofluids. J. Magn. Mater. 289: 21-24.

[6] Kang Y. S., Risbud S., Rabolt J. F., Stroeve P., (1996), Synthesis and characterization of nanometer-size Fe₃O₄ and γ-Fe₂O₃ particles. Chem. Mater. 8: 2209-2211.

[7] Zhang S., Chen X. J., Gu C. R., Zhang Y., Xu J. D., Bian Z. P., Yang D., Gu N., (2009), The effect of Iron Oxide magnetic nanoparticles on smooth muscle cells. Nanoscale Res. Lett. 4: 70-77.

[8] Srivastava R., Yadav B. C., (2012), Nanaostructured ZnO, ZnO-TiO₂ and ZnO-Nb₂O₅ as solid-state humidity sensor. Adv. Mat. Let. 3: 197-203.

[9] Chen L., Pang X., Yu G., Zhang J., (2010), In-situ coating of MWNTs with sol-gel TiO₂ nanoparticles. Adv. Mat. Lett. 1: 75-78.

[10] Askarinezhad A., Morsali A., (2008), Syntheses and characterization of CdCO₃ and CdO nanoparticles by using a sonochemical method. Mater. Lett. 62: 478-482.

[11] Sun Z. Y., Yuan H. Q., Liu Z. M., Han B. X., Zhang X. R., (2005), A highly efficient chemical sensor material for H₂S : α-Fe₂O₃ nanotubes fabricated using carbon nanotube templates. Adv. Mat. 17: 2993-2997.

[12] Jing Z. H., Wang Y., Wu S. H., (2006), Preparation and gas sensing properties of pure and doped γ-Fe2O3 by an anhydrous solvent method. Sens. Actuators. 113: 177-181.

[13] Lee E. T., Jang G. E., Kim C. K., Yoon D. H., (2001), Fabrication and gas sensing properties of Fe₂O₃ thin film prepared by plasma enhanced chemical vapor deposition (PECVD). Sens. Actuators Chem. 77: 221-227.

[14] Lim I. S., Jang F. E., Kim C. K., Yoon D. H., (2001), Fabrication and gas sensing characteristics of pure and Pt-doped γ-Fe₂O₃ thin film. Sens. Actuators. 77: 215-220.

[15] Dai Z. R., Pan Z. W., Wang Z. L., (2003), Novel nanostructures of functional oxides synthesized by thermal evaporation. Adv. Mat. 13: 9-23.

[16] Zheng W., Li Z. Y., Zhang H. N., Wang W., Wang Y., Wang C., (2009), Electrospinning route for α-Fe₂O₃ ceramic nanofibers and their Gas sensing properties. Mater. Res. Bull. 44: 1432-1436.

[17] Segadaes A. M., (2006), Oxide powder synthesis by the combustion route. Eur. Ceram. News Lett. 9: 1-5.

[18] Mukasyan A. S., Rogachev A. S., (2008), Discrete reaction waves: Gasless combustion of solid powder mixtures. Prog. Energy Comb. Sci. 34: 377-416.

[19] Kleiman-Shwarsctein A., Huda M. N., Walsh A., Yan Y., Stucky G. D., Hu Y.-S., Al-Jassim M. M., McFarland E. W., (2010), Electrodeposited aluminum-doped α-Fe₂O₃ photoelectrodes: Experiment and theory. Chem. Mater. 22: 510-517.

[20] Kleiman-Shwarsctein A., Hu Y.-S., Forman A. J., Stucky G. D., McFarland E.W., (2008), Electrodeposition of α-Fe₂O₃ doped with Mo or Cr as photoanodes for photocatalytic water splitting. J. Phys. Chem. 112: 15900-15907.

[21] Glasscock J. A., Barnes P. R. F., Plumb I. C., Savvides N., (2007), Enhancement of photoelectrochemical hydrogen production from hematite thin films by the introduction of Ti and Si. J. Phys. Chem. 111: 16477-16488.

[22] Cesar I., Kay A., Gonzales Martinez J. A., Graetzel M., (2006), Translucent thin film Fe₂O₃ photoanodes for efficient water splitting by sunlight: Nanostructure-Directing effect of Si-Doping. J. Am. Chem. Soc. 128: 4582-4583.

[23] Ingler W. B., Baltrus J. P., Khan S. U. M., (2004), Photoresponse of p-type zinc-doped iron (III) oxide thin films. J. Am. Chem. Soc. 126: 10238-10239.

[24] Goyal G., Dogra A., Rayaprol S., Kaushik S. D., Siruguri V., Kishan H., (2012), Structural and magnetization studies on nanoparticles of Nd doped α-Fe₂O₃. Mat. Chem. Phys. 134: 133-138.

[25] Bahaa Abu-Zied M., Asiri A. M., (2014), Synthesis of Dy₂O₃ nanoparticles via hydroxide precipitation: Effect of calcination temperature. J. Rare Earths. 32: 259-264.

[26] Kanga J-G., Seog Gwagb J., Sohn Y., (2015), Synthesis and characterization of Dy(OH)₃ and Dy₂O₃ nanorods and nanosheets. Ceram. Int. 41: 399-4006.

[27] Pinkas J., Reichlova V., Zboril R., Moravec Z., Bezdicka P., Matejkova J., (2008), Sonochemical synthesis of amorphous nanoscopic iron (III) oxide from Fe(acac)₃. J. Ultrason. Sonochem. 15: 257-264.

[28] Almeida T., Fay M., Zhu Y. Q., Brown P. D., (2009), Process map for the hydrothermal synthesis of α-Fe₂O₃ nanorods. J. Phys. Chem. 113: 18689-18698.

[29] Zhang G. Y., Xu Y.Y., Gao D. Z., Sun Y. Q., (2011), α-Fe₂O₃ nanoplates: PEG-600 assisted hydrothermal synthesis and formation mechanism. J. Alloys. Compd. 509: 885-890.

[30] Zhang G. Y., Feng Y., Xu Y. Y., Gao D. Z., Sun Y. Q., (2012), Controlled synthesis of mesoporous α-Fe₂O₃ nanorods and visible light photocatalytic property. Mate. Res. Bull. 47: 625-630.

[31] Darezereshki E., (2011), One-step synthesis of hematite (α-Fe₂O₃) nano-particles by direct thermal-decomposition of maghemita. Mater. Lett. 65: 642-645.

[32] Gu F., Wang Sh. F., Lu M. K., Zhou G. J., Xu D., Yuan D. R., (2004), Structure evaluation and highly enhanced luminescence of Dy³⁺-doped ZnO nanocrystals by Li⁺ doping via combustion method.  Langmuir. 20: 3528-3531.

[33] Sahoo S. K., Agarwal K., Singh A. K., Polke B. G., Raha K. C., (2010), Characterization of γ- and a-Fe₂O₃ nano powders synthesized by emulsion precipitation-calcination route and rheological behaviour of a-Fe₂O₃. Int. J. Eng. Sci. Tech. 2: 118-126.

[34] ChangLiang H., HongYe Z., ZhenYu S., ZhiMin L., (2010), Chitosan-mediated synthesis of mesoporous α-Fe₂O₃ nanoparticles and their applications in catalyzing selective oxidation of cyclohexane. Sci. China. Chem. 53: 1502-1508.

[35] Yogi A., Varshney D., (2013), Magnetic and structural properties of pure and Cr-doped haematite: α-Fe_2−xCr_xO₃ (0 ≤ x ≤ 1). J. Adv. Ceram. 2: 360-369.

[36] Rabanal M. E., Rez A. Va., Levenfeld B., Torralba J. M., (2003), Magnetic properties of Mg-ferrite after milling process. J. Mater. Process. Technol. 143: 470-474.

[37] Huang Y., Tang Y., Wang J., Chen Q., (2006), Synthesis of MgFe₂O₄ nanocrystallites under mild conditions. Mater. Chem. Phys. 97: 394-397.