Anti-corrosion and Anti-bacterial properties investigation of Graphene Oxide coating on AISI 304 stainless steel

Journal of Applied Chemical Research

دوره 15، شماره 3، مهر 2021، صفحه 8-20   

نوع مقاله: Research Paper

نویسنده

Fatemeh Abdi^*

Department of Engineering Sciences, Faculty of Advanced Technologies, University of Mohaghegh Ardabili, Namin, Iran

چکیده

In  this  work,  the  corrosion  resistance  and  antibacterial  properties  of  Graphene  Oxide  were investigated. Hummer’s method was used for production of Graphene Oxide on AISI 304 stainless steel,  and  its  formation  was  tested  by  Raman  spectroscopy.  Electrochemical  Impedance spectroscopy  (EIS)  and  Polarization  tests  in  3.5%  NaCl  solution  were  carried  out  for  corrosion inhibition studies of the produced samples. Results of corrosion measurements revealed that coating of GrapheneOxide on stainless steel greatly improves its corrosion resistance. Surface morphology of the samples after corrosion tests was examined by scanning electron microscope analysis (SEM).
The equivalent circuit of all samples was obtained, using the EIS data. Japanese Industry Standard test  Methods  was  used  for  antibacterial  properties  investigation  against  gram  negative  E.  coli bacteria.   The  results  of  antibacterial  analysis  showed  that  Graphene  Oxide  with anti-corrosion property, is promising material for antibacterial applications.

کلیدواژه‌ها

Graphene Oxide؛ Corrosion؛ Electrochemical impedance spectroscopy؛ Equivalent circuit؛ E. coli

مراجع

[1]. N. R. Baddoo, Journal of Constructional Steel Research, 64, 1199 (2008).
[2]. K.M. Perkins, M.R. Bache, Int. J. Fatigue, 22, 1499(2005).
[3]. S. E. Ziemniak, M. Hanson, Corros. Sci., 44, 2209 (2002).
[4]. H. Zhang, Y. L. Zhao, Z. D. Jiang, Mater. Lett., 59, 3370 (2005).
[5]. D. H. Mesa, A. Toro, A. Sinatora, A. P. Tschiptschin, Wear., 255, 139 (2003).
[6]. H. Savaloni, M. Habibi, Applied Surface Science., 258, 103 (2011).
[7]. C. Liu, G. Lin, D. Yang, M. Qi, Surf. Coat. Technol., 200, 4011 (2006).
[8]. V. H. V. Sarmento, M. G. Schiavetto, P. Hammer, A. V. Benedetti, C. S. Fugivara, P. H.
Suegama, S. H. Pulcinelli, C. V. Santilli, Surf. Coat. Technol., 204, 2689 (2010).
[9]. D. Pech, P. Steyer, J. P. Millet, Corros. Sci., 50, 1492 (2008).
[10]. A. R. Grayeli, H. Savaloni, Applied Surface Science., 258, 9982 (2012).
[11]. W. Haitao, Z. Qi, Y. Huashun, Z. Zhenya, C. Hongwei, M. Guanghui, steel, 15, 457 (2009).
[12]. K. Asami, K. Hashimoto, Corros. Sci., 45, 2263 (2003).
[13]. M. I.Katsnelson, I. V.Grigorieva, S. V.Dubonos, A. A. Firsov, Nature, 438, 197 (2005).
[14]. K. S.Novoselov, A. K.Geim, M S. V.orozov, D.Jiang, Y.Zhang, S. V.Dubonos, I.V.Grigorieva, A. A. Firsov, Science, 306, 666 ( 2004).
[15]. Y. B.Zhang, Y. W.Tan, H. L. Stormer, P.Kim, Nature, 438, 201 (2005).
[16]. X. K. Lu, M. F.Yu, H.Huang, R. S. Ruoff, Nanotechnology, 10, 269 (1999).
[17]. J. S.Bunch, S. S.Verbridge, J. S.Alden, A. M.van der Zande, J. M.Parpia, H. G.Craighead, P. L.
McEuen,.Nano Lett, 8, 2458 (2008). 

[18]. S. Chen, L.Brown, M.Levendorf, W.Cai, S. Y. Ju, J.E. worth, X. Li, C. W. Magnuson, A.
Velamkanni, R. D. Piner, ACS Nano, 5, 1321 (2011).
[19]. P. Misaelides, A. Hatzidimitriou, F. Noli, A.D. Pogrebnjak, Y.N. Tyurin, S. Kosionidis,
Surf. Coat. Technol., 180, 290 (2004).
[20]. D. Prasai, J.C. Tuberquia, R.R. Harl, G.K. Jennings, K.I. Bolotin, ACS Nano, 6, 1102 (2012).
[21]. R.K.S. Raman, P.C. Banerjee, D.E. Lobo, H. Gullapalli, M. Sumandasa, A. Kumar,
L.Choudhary, R. Tkacz, P.M. Ajayan, M. Majumder, Carbon, 50, 4040 (2012).
[22]. N.T. Kirkland, T. Schiller, N. Medhekar, N. Birbilis, Corrosion Science, 56 ,1 (2012)
[23]. H. Yun, T. D. N. Phan, V. H. Pham, H. Kweon, J. S. Chung, B. Lee, E. W. Shin, Mater. Res.
Bull.,47, 2988 (2012).
[24]. S.C. Sahu, A.K. Samantara, M.Seth, S.Parwaiz, B. P. Singh, P.C. Rath, B.K.Jena,
Electrochemistry Communications, 32, 22 (2013).
[25]. S.J. R. Prabakar, Y.H. Hwang, E. G. Bae, D.K.Lee, Carbon, 52, 128 (2013).
[26]. S.A. Onaizi, S. S. J. Leong,Biotech. Advances, 29, 67(2011).
[27]. R. Dastjerdi, M. Montazer, Colloids and Surfaces B: Biointerfaces , 79, 5 (2010).
[28]. M.S .Usman, M.E. E.l. Zowalaty, K. Shameli, N. Zainuddin, M. Salama, and N. A. Ibrahim, Int
J Nanomedicine, 8, 4467 (2013).
[29]. M. M.Almoudi,A. S.Hussein,M. I.A. Hassan,, N.M. Zain,, The Saudi Dental Journal, 30, 4,
283 (2018).
[30]. Y. Xie, Y. He, P. L. Irwin, T. Jin, and X.Shi, Appl Environ Microbiol, 77, 2325 (2011).
[31]. N. Manjula, M. Suganya, D. Prabha, S. Balamurugan, J. Srivind, V. S. Nagarethinam, A. R.
Balu, Journal of Materials Science: Materials in Electronics, 28, 7615 (2017).
[32]. H. Kawakami, K. Yoshida, Y. Nishida, Y. Kikuchi and Y. Sato, ISIJ International, 48, 1299
(2008).
[33]. J.Yanab, L. Zhengb, K.Hu, L. Li,C. Li,L. Zhud, H. Wang,Y.Xiao,S. Wua,J. Liu,B.
Zhang,F.Zhange, European Polymer Journal, 110, 41 (2019)
[34]. A. M. Bonilla, M. F.García, Progress in Polymer Science, 37, 281(2012).
[35]. S. Pandey, International Journal of Scientific & Engineering Research, 8, 1697(2017)
[36]. P. Kumar, P.Huo, R. Zhang, and B. Liu, Nanomaterials, 9, 737 (2019).
[37]. W.C. Hou, P.L. Lee, Y.C. Chou and Y.S. Wang, Environ. Sci. Nano, 4, 647 (2017).
[38]. D.R. Dreyer, S. Park, C.W. Bielawski, R.S. Ruoff. Chem. Soc. Rev. 39, 228 (2010).

[39]. X. Zhang, J. Yin, C. Peng, W. Hu, Z. Zhu, W. Li, C. Fan, Q. Huang, Carbon,49, 986 (2011).
[40]. ON Ruiz, ACS Nano, 5, 8100 (2011)
[41]. S. Pei, H.M Cheng, Carbon, 50, 3210 (2012).

[42]. E. E. Stansbury, R. A. Buchanan, Fundamentals of Electrochemical Corrosion, ASM, Ohio
(2000).
[43]. F.Abdi, H.Savaloni, Trans. Nonferrous Met. Soc. China, 27, 701(2017)
[44]. E. Poorqasemi, O. Abootalebi, M. Peikari, F. Haqdar, Corros. Sci., 51, 1043 (2009).
[45]. R. Kelly, J. R. Scully, D. Shoesmith, R. G. Buchheit, Electrochemical techniques in corrosion
science and engineering, Dekker, New York (2002).
[46]. A.Stich, S. Buhl, and C. Bulitta, Current Directions in Biomedical Engineering, 4, 229 (2018).