The Effect of Reverse Pulse Plating and Lanthanum Addition in Plating Bath on Corrosion Resistance of Austenitic Steel in Chlorine Solution

Journal of Advanced Materials and Processing

دوره 9، شماره 3، آبان 2021، صفحه 23-34   

نوع مقاله: Research Paper

نویسندگان

Leila Bakhtiari؛ Abdolhamid Jafari^* ؛ Shahriyar Sharafi

Materials Science and Engineering Dept., Shahid Bahonar University, Jomhori-e-Eslami Blvd., Kerman, Iran

چکیده

The 316L nickel-chrome molybdenum austenitic stainless steel is commonly employed in various industries. This type of steel is particularly of interest in chemical industries, especially in harsh and corrosive environmental conditions. Although 316L stainless steel has good mechanical and corrosive characteristics, it fails to perform well in chlorine-containing aqueous environments. To overcome this issue, a Ni-La-Cr-Fe layer is applied to the 316L steel using the electroplating method. In addition, the reverse pulse plating method is used to control the ion deposition kinetics. The plating current application duration (on-time), the current disruption duration (off-time), and (TRev) are the control parameters of the duration and polarity of the pulse. Finally, the coated layer acquires an average thickness of 6.83 after applying on-time and off-time repeatedly and performing SEM and polarization tests in 1.5% solution at 50 Celcius degrees. Furthermore, the desired surface morphology is achieved, and corrosion resistance is 160 times higher than 316 bare steel. Applying the reverse pulse plating method, adding beneficial compounds of saccharin and SDS, and using lanthanum chloride in the plating bath are the essential reasons to successfully add a coating layer on the 316 bare steel.

کلیدواژه‌ها

coating؛ stainless steel. lanthanum؛ pulse reverse plating؛ corrosion

مراجع

[1] D. Krouse, N. Laycock, C. Padovani, “Modelling pitting corrosion of stainless steel in atmospheric exposures to chloride containing environments”, Corrosion Engineering, Science and Technology, Vol. 49, No. 6, 2014, pp. 521-528.

[2] B. Lorsbach, E. Schmitz, “Influence of test parameters of potentiodynamic current density measurements on the determination of the pitting corrosion resistance of austenitic stainless steels”, Materials and Corrosion, Vol. 69, No. 1, 2018, pp. 37-43.

[3] G. Bai, S. Lu, D. Li, Y. Li, “Influences of niobium and solution treatment temperature on pitting corrosion behaviour of stabilised austenitic stainless steels”, Corrosion Science, Vol. 108, 2016, pp. 111-124.

[4] N.T Nga, T. Shinohara, T.H. Le, “Effects of Environment Factors on Stress Corrosion Cracking of Austenitic Stainless Steels in Atmospheric Environments”, Zairyo-to-Kankyo, Vol. 66, No. 6, 2017, pp. 209-213.

[5] H.S Klapper, J. Stevens, G. Wiese, “Pitting Corrosion Resistance of CrMn Austenitic Stainless Steel in Simulated Drilling Conditions—Role of pH, Temperature, and Chloride Concentration”, Corrosion, Vol. 69, No. 11, pp. 1095-1102.

[6] B. R. Tzaneva, M. H. Loukaycheva, L. B. Fachikov, L. Ts. Jekova, “ Effect of chloride ions on corrosion behaviour of austenitic nickel and nickel free stainless steels in phosphoric acid solutions”, Corrosion Engineering, Science and Technology, Vol. 50, No. 8, 2015, pp. 568-578.

[7] H.S Klapper, C. Menendez, S. Jesse, “Pitting Corrosion Resistance Influencing Corrosion Fatigue Behavior of an Austenitic Stainless Steel in Chloride-Containing Environments”, Corrosion, Vol. 76, No. 4, 2020, pp. 398-410.

[8] R. Yamanoglu, E. Fazakas, F. Ahnia, D. Alontseva, F. Khoshnaw, “Pitting Corrosion behaviour of Austenitic Stainless-Steel Coated on Ti₆A_l4V Alloy in Chloride Solutions”, Advances in Materials Science, Vol. 21, No. 2, 2021, pp. 5-15.

[9] R. T. Loto, “Data on the Corrosion Resistance and Polarization Behaviour of Lean Austenitic and Ferritic Stainless Steels in Neutral Chloride Media”, Oriental Journal of Chemistry, Vol. 35, No. 3, 2019, pp. 1138-1142.

[10] M.H. Jang, J.Y. Kang, J.H. Jang, T.H. Lee, C. Lee, “Hot deformation behavior and microstructural evolution of alumina-forming austenitic heat-resistant steels during hot compression”, Materials Characterization, Vol. 123, 2017, pp. 207-217.

[11] D.B Park, S.M Hong, K.H Lee, M.Y Huh, J.Y Suh, S.C Lee, WS Jung, “High-temperature creep behavior and microstructural evolution of an 18Cr₉Ni₃CuNbVN austenitic stainless Steel”, Materials Characterization, Vol. 93, 2014, pp. 52-61.

[12] L. Liu, S. Wu, Y. Chen, et al, “Oxidation behavior of RE-modified nickel-based superalloy between 952℃ and 1150℃ in air. Transactions of Nonferrous”, Metals Society of China, Vol. 26, 2016, pp. 1163-1169.

[13] H.T Mallikarjuna, W.F Caley, N.L Richards, “Oxidation Kinetics and Oxide Scale Characterization of Nickel-Based Superalloy IN738LC at 900°C”, Journal of Materials Engineering & Performance, Vol. 26, 2017, pp. 1-9.

[14] Z. Zheng, S. Wang, J. Long, J. Wang, K. Zheng, “Effect of Rare Earth Elements on High Temperature Oxidation Behavior of Austenitic Steel”, Corrosion Science, Vol. 164, 2020, pp. 108-155.

[15] S. R. J Saunders, J. R. Nicholls, “Coatings and surface treatments for high temperature oxidation resistance”, Metal Science Journal, Vol. 5, 2013, pp. 780-798.

[16] A. Karimi, R. Soltani, M. Ghambari, et al, “High temperature oxidation resistance of plasma sprayed and surface treated YSZ coating on Hastelloy X”, Surface & Coatings Technology, Vol. 321, 2017, pp. 378-385.

[17] H. Liu, X. Zhang, Y. Jiang, et al, “Microstructure and high temperature oxidation resistance of in-situ synthesized TiN/Ti₃Al intermetallic composite coatings on Ti₆Al₄V alloy by laser cladding process”, Journal of Alloys & Compounds, Vol. 670, 2016, pp. 268-274.

[18] W. Hansal, “Pulse plating as a core technology of surface finishing in the twenty-first century: review of the Eighth European Pulse Plating Seminar”, Transactions of the IMF, Vol. 96, No. 3, 2018, pp. 115-117.

[19] J.-C. Puippe, “Unconventional pulse plating parameters for surface area measurement applications”, Transactions of the IMF, Vol. 99, No. 1, 2021, pp. 17-22.

[20] C. Y. Chen, C. C. Hsu, U. W. Liu, C. A. Huang, “Characterization of Cr-Ni Multilayers from Chromium(III)-Nickel(II) Baths Using Pulse-Current Plating”, ECS Transactions, Vol. 2, No. 3, 2019, pp. 413-418.

[21] J. Zhang, C. Su, X. Chen, H. Liu, L. Zhang, “First-principles study on pitting corrosion of Al deoxidation stainless steel with rare earth element (La) treatment”, Materials Today Communications, Vol. 27, 2021, pp. 102-114.

[22] Y. C. Yu, S. H. Zhang, S. B. Wang, “Effects of Cerium on the Inclusions and Pitting Corrosion Behavior of 434 Ferritic Stainless Steel”, High Temperature Materials and Processe, Vol. 37, No. 9, 2018, pp. 807-814.

[23] W. Zheng, X. Yan, S. Xiong, G. Wang, G. Li, “Pitting corrosion behavior of cerium treated HSLA steel induced by sulfide inclusions in 3.5 wt% NaCl solution”, Journal of Rare Earths, Vol. 39, No. 3, 2021, pp. 348-356.

[24] N. Yin, C.L. Jing, H.B Li, R.S Chu, B. Chen, “Effect of Rare Earth Elements on the Inclusion Behavior in Low Alloy Structural Steel”, Materials Science Forum, Vol. 944, 2019, pp. 364-372.

[25] X. Cheng, Z. Jiang, D. Wei, et al, “Characteristics of oxide scale formed on ferritic stainless steels in simulated reheating atmosphere”, Surface & Coatings Technology, Vol. 258, 2014, pp. 257-267.

[26] Q. Wang, Q. Yao, Y. Wang, et al, “Research on the oxidation behavior of novel γ/γ'-strengthened Co-9Al-10W alloys combined with chromium and rare earth elements”, Journal of Materials Research, Vol. 31, 2016, pp. 3332-3344.

[27] X. Xing, H. Wang, P. Lu, Z. Han, “Influence of rare earths on electrochemical corrosion and wear resistance of RE–Cr/Ti pack coatings on cemented 304 stainless steel”, Surface And Coating Technology, Vol. 291, 2016, pp. 151-160.

[28] C. Liu, R.I Revilla, Z. Liu, D. Zhang, X. Li, H. Terryn, “Effect of inclusions modified by rare earth elements (Ce, La) on localized marine corrosion in Q460NH weathering steel”, Corrosion Science, Vol. 129, 2017, pp. 82-90.

[29] D. Xueliang, W. Deren, Z. Yangqing, “ Effect of mechanical attrition on microstructure and properties of electro-deposition coatings on NdFeB”, Journal of Rare Earths, Vol. 32, No. 9, 2014, pp. 867-873.

[30] J. Guo, L. Bingwen, H. Dingding, C. Xiufang, et al, “Influence of rare earths addition on residual stress of Fe-based coating prepared by brush plating technology”, Journal of Rare Earths, Vol. 34,  2016, pp. 336-345.

[31] M.A.M. Ibrahim, R.S. Bakdash, “New non-cyanide acidic copper electroplating bath based on glutamate complexing agent”, Surface Coating Technology, Vol. 282, 2015, pp. 139–148.

[32] Brian Hinderliter, “Response of Electrochemical Impedance Spectroscopy to Evolving Coating Systems”, ECS. Transactions, Vol. 41, No. 15, 2019, pp. 39-51.

[33] N. Imaz, M. Ostra, M. Vidal, J.A. Díez, M. Sarret, E. García-Lecina, “Corrosion behaviour of chromium coatings obtained by direct and reverse pulse plating electrodeposition in NaCl aqueous solution”, Corrosion Science, Vol. 78, 2014, pp. 251-259.

[34] M.S. Chandrasekar, Malathy Pushpavanam, “Pulse and pulse reverse plating—Conceptual, advantages and applications”, Electrochimica Acta, Vol. 53, No. 8, 2008, pp. 3313-3322.

[35] G. Wang, D. Li, Y. Zuo, Y. Tang, X. Zhang, X. Zhao, “The Improvement of Hardness and Corrosion Resistance of Electroplated Pd-Ni Film on 316L Stainless Steel by CeCl₃”, Coatings, Vol. 10, No. 2, 2020, pp. 161-171.

[36] R. Gupta, A. Sharma, U. Pandel, L. Ratke, “Effect of stirring speed on microstructure of A356 alloy cast through rheometal process”,  International Journal of Materials Research, Vol. 108, No. 8, 2017, pp. 648-655.

[37] P. Marcolin, M. Longhi, L. P. Zini, B. Proença, et al, “ Influence of the pH and Stirring Speed of the Electrodeposition Bath in the Performance of Zinc and Zinc-Nanocomposite Coatings”, Materials Science Forum, Vol. 899, 2017, pp. 283-288.

[38] S. An, Y.I Kim, H.S Jo, M.W Kim, M.W Lee, A.L Yarin, et al, “Silver-decorated and palladium-coated copper electroplated fibers derived from electrospun polymer nanofibers”, Chem. Eng. J., Vol. 327, 2017, pp. 336–342.

[39] Y. Kamimoto, S. Okura, T. Hagio, T. Wada, H. Tanaka, et al, “Nickel–carbon composite plating using a Watts nickel electroplating bath. SN Applied Sciences”, Vol. 2, No. 2, 2020, pp. 1-6.

[40] M. Mohammadi, M. Ghorbani, “Wear and corrosion proper‑ ties of electroless nickel composite coatings with PTFE and/or MoS2 particles”, J. Coat Technol Res, Vol. 8, 2011, pp. 527–533

[41] W. Dan, Y. Cheng, J. Huiming, J. Zhang, J. Gao, “Influence of LaCl3 addition on microstructure and properties of nickel-electroplating coating”, Journal of Rare Earths, Vol. 31, No. 2, 2013, pp. 209-214.