اخبار و اعلانات

 آمار

تعداد نشریات418
تعداد شماره‌ها9,997
تعداد مقالات83,560
تعداد مشاهده مقاله77,801,288
تعداد دریافت فایل اصل مقاله54,843,919
Nouri, Esmaiel, Shahmiri, Mohammad, Rezaie, Hamid Reza, Talayian, Fatemeh. (1391). The effect of alumina content on the structural properties of ZrO2-Al2O3 unstabilized composite nanopowders. نشریه علمی پژوهشی دانشگاه آزاد اسلامی, 3(1), 124-131. doi: https://doi.org/10.1186/2228-5547-3-17
Esmaiel Nouri; Mohammad Shahmiri; Hamid Reza Rezaie; Fatemeh Talayian. "The effect of alumina content on the structural properties of ZrO2-Al2O3 unstabilized composite nanopowders". نشریه علمی پژوهشی دانشگاه آزاد اسلامی, 3, 1, 1391, 124-131. doi: https://doi.org/10.1186/2228-5547-3-17
Nouri, Esmaiel, Shahmiri, Mohammad, Rezaie, Hamid Reza, Talayian, Fatemeh. (1391). 'The effect of alumina content on the structural properties of ZrO2-Al2O3 unstabilized composite nanopowders', نشریه علمی پژوهشی دانشگاه آزاد اسلامی, 3(1), pp. 124-131. doi: https://doi.org/10.1186/2228-5547-3-17
Nouri, Esmaiel, Shahmiri, Mohammad, Rezaie, Hamid Reza, Talayian, Fatemeh. The effect of alumina content on the structural properties of ZrO2-Al2O3 unstabilized composite nanopowders. نشریه علمی پژوهشی دانشگاه آزاد اسلامی, 1391; 3(1): 124-131. doi: https://doi.org/10.1186/2228-5547-3-17

The effect of alumina content on the structural properties of ZrO2-Al2O3 unstabilized composite nanopowders

International Journal of Industrial Chemistry
دوره 3، شماره 1، اسفند 2012، صفحه 124-131
نوع مقاله: research article
شناسه دیجیتال (DOI): https://doi.org/10.1186/2228-5547-3-17
نویسندگان
Esmaiel Nouri* 1؛ Mohammad Shahmiri1؛ Hamid Reza Rezaie1؛ Fatemeh Talayian2
1Department of Materials and Metallurgical Engineering, Iran University of Science and Technology (IUST), Narmak, Tehran, 16846-13114, Iran
2Department of Materials Engineering, Sahand University of Technology, Tabriz, 11111-53317, Iran
چکیده
In this research, a sol–gel process was used to synthesize zirconia-alumina (ZrO2-Al2O3) composite nanopowders containing 10, 20, and 50 mol% alumina (Al2O3) without any stabilizer. Zirconium acetate hydroxide and aluminum isopropoxide were employed as precursors. The produced composite nanopowders were characterized using a Brunauer-Emmett-Teller (BET) surface area analyzer, Fourier transform infrared (FTIR) spectroscopy, thermogravimetric/differential thermal analysis, X-ray diffraction analysis (XRD), and scanning electron microscopy (SEM). The BET results showed a decrease in surface area and average particle size and an increase in pore size with increasing Al2O3 content. FTIR, in corroboration with XRD, confirms the crystallization of corundum (α-Al2O3) as one of the alumina phases. The X-ray studies showed that an increase in Al2O3 content shifted the tetragonal zirconia (t-ZrO2)-phase crystallization to higher temperatures. Microstructural characterization by SEM depicted that the particles tend to be more agglomerated with increasing Al2O3 content.
کلیدواژه‌ها
Sol–gel process؛ Heat treatment؛ ZrO2-Al2O3 composite nanopowders؛ α-Al2O3؛ t-ZrO2