Roosta, Mostafa, Baharvandi, Hamidreza, Abdizade, Hossein. (1391). An experimental investigation on the fabrication of W-Cu composite through hot-press. نشریه علمی پژوهشی دانشگاه آزاد اسلامی, 3(1), 180-185. doi: https://doi.org/10.1186/2228-5547-3-10
Mostafa Roosta; Hamidreza Baharvandi; Hossein Abdizade. "An experimental investigation on the fabrication of W-Cu composite through hot-press". نشریه علمی پژوهشی دانشگاه آزاد اسلامی, 3, 1, 1391, 180-185. doi: https://doi.org/10.1186/2228-5547-3-10
Roosta, Mostafa, Baharvandi, Hamidreza, Abdizade, Hossein. (1391). 'An experimental investigation on the fabrication of W-Cu composite through hot-press', نشریه علمی پژوهشی دانشگاه آزاد اسلامی, 3(1), pp. 180-185. doi: https://doi.org/10.1186/2228-5547-3-10
Roosta, Mostafa, Baharvandi, Hamidreza, Abdizade, Hossein. An experimental investigation on the fabrication of W-Cu composite through hot-press. نشریه علمی پژوهشی دانشگاه آزاد اسلامی, 1391; 3(1): 180-185. doi: https://doi.org/10.1186/2228-5547-3-10

An experimental investigation on the fabrication of W-Cu composite through hot-press

International Journal of Industrial Chemistry
دوره 3، شماره 1، اسفند 2012، صفحه 180-185
نوع مقاله: research article
شناسه دیجیتال (DOI): https://doi.org/10.1186/2228-5547-3-10
نویسندگان
Mostafa Roosta* 1؛ Hamidreza Baharvandi1؛ Hossein Abdizade2
1Malek-Ashtar University of Technology, P.O. Box 13336–95711, Tehran, Iran
2School of Metallurgy and Materials Engineering, University of Tehran I. R., Tehran, Iran
چکیده
In this paper the feasibility of fabricating W-Cu composite by hot-press has been studied and the best parameters for hot-pressing were acquired. W/20 vol%Cu composite was successfully prepared by this process, in which at first the powder of tungsten and copper, containing 20% vol copper were mixed in a ball mill for 3 h at rotation speed of 200 rpm. Then the mixed powders were hot-pressed for 3 h at a compact pressure of 30 MPa and temperatures of 1,250°C, 1,350°C, and 1,450°C. The composites made have been investigated and revealed the making W-Cu composite with good properties included density, hardness, modules of elasticity, flexural strength, and microstructure. Also, the sample made at 1,450°C possesses better properties, and its microstructure showed the tungsten matrix and the copper reinforcement separately; the X-ray diffraction patterns showed that no compound has been formed between W and Cu.
کلیدواژه‌ها
Tungsten-copper؛ Composite materials؛ Hot-press