Salah, Merah, Lahcène, Larabi, Omar, Abderrahim, Yahia, Harek. (1396). Study of corrosion inhibition of C38 steel in 1 M HCl solution by polyethyleneiminemethylene phosphonic acid. نشریه علمی پژوهشی دانشگاه آزاد اسلامی, 8(3), 263-272. doi: https://doi.org/10.1007/s40090-017-0123-2
Merah Salah; Larabi Lahcène; Abderrahim Omar; Harek Yahia. "Study of corrosion inhibition of C38 steel in 1 M HCl solution by polyethyleneiminemethylene phosphonic acid". نشریه علمی پژوهشی دانشگاه آزاد اسلامی, 8, 3, 1396, 263-272. doi: https://doi.org/10.1007/s40090-017-0123-2
Salah, Merah, Lahcène, Larabi, Omar, Abderrahim, Yahia, Harek. (1396). 'Study of corrosion inhibition of C38 steel in 1 M HCl solution by polyethyleneiminemethylene phosphonic acid', نشریه علمی پژوهشی دانشگاه آزاد اسلامی, 8(3), pp. 263-272. doi: https://doi.org/10.1007/s40090-017-0123-2
Salah, Merah, Lahcène, Larabi, Omar, Abderrahim, Yahia, Harek. Study of corrosion inhibition of C38 steel in 1 M HCl solution by polyethyleneiminemethylene phosphonic acid. نشریه علمی پژوهشی دانشگاه آزاد اسلامی, 1396; 8(3): 263-272. doi: https://doi.org/10.1007/s40090-017-0123-2

Study of corrosion inhibition of C38 steel in 1 M HCl solution by polyethyleneiminemethylene phosphonic acid

International Journal of Industrial Chemistry
دوره 8، شماره 3، آذر 2017، صفحه 263-272
نوع مقاله: research article
شناسه دیجیتال (DOI): https://doi.org/10.1007/s40090-017-0123-2
نویسندگان
Merah Salah* 1، 2؛ Larabi Lahcène1؛ Abderrahim Omar3؛ Harek Yahia3
1Laboratory of Analytical Chemistry and Electrochemistry, Department of Chemistry, Faculty of Science, Tlemcen University, Tlemcen, Algeria
2Department of Process Engineering, Faculty of Technology, Saϊda University, Saϊda, Algeria
3Laboratory of Separation and Purification Technology, Department of Chemistry, Faculty of Science, Tlemcen University, Tlemcen, Algeria
چکیده
A new class of corrosion inhibitors, namely, polyethyleneiminemethylene phosphonic acid (PEIMPA), was synthesized and its inhibiting action on the corrosion of C38 steel in 1 M HCl at 30 °C was investigated by various corrosion monitoring techniques such as weight loss measurements, potentiodynamic polarization, linear polarization resistance (Rp), and surface analysis (SEM and EDX) which are used to characterize the steel surface. Weight loss measurements revealed that the presence of PEIMPA increases the inhibition efficiency by decreasing the corrosion rate. Tafel polarization study showed that the inhibitor acts as a mixed-type inhibitor. Adsorption of PEIMPA on the carbon steel surface was found to obey the Langmuir isotherm. Some thermodynamic functions of dissolution and adsorption processes were also determined and discussed. The SEM results showed the formation of protective film on the mild steel surface in the presence of PEIMPA. The results obtained from different tested techniques were in good agreement.
کلیدواژه‌ها
Corrosion؛ Inhibition؛ C38 steel؛ Phosphonic acid