Survey and Evaluation of Hardystonite Nanostructure (HTN) Bioactivity in Biomedical Engineering | ||
Journal of Nanoanalysis | ||
مقالات آماده انتشار، پذیرفته شده، انتشار آنلاین از تاریخ 05 خرداد 1401 | ||
نوع مقاله: Original Research Paper | ||
شناسه دیجیتال (DOI): 10.22034/jna.2022.1955260.1297 | ||
نویسنده | ||
hassan GHEISARI* | ||
Advanced Materials Research Center, Department of Materials, Najafabad Branch, Islamic Azad University, Najafabad, Iran | ||
چکیده | ||
Hardystonite (HT) is a monoclinic pyroxene mineral with composition Ca2ZnSi2O7. Lately, Hardystonite (HT) has been introduced as a bioceramics due to its best bioactivity and biocompatibility. It has a good strength and toughness than those of hydroxyapatite (HA). In this project, bioactivity of hardystonite (HT) powder were evaluated and investigated. For synthesized of hardystonite (HT) powder, Zinc (Zn), calcite (CaCO3) and nano silicium (SiO2) powders was mechanically activate for different times. After that, the prepared powders were blended with ammonium chloride (NH4Cl) and put on various temperatures. In this part, for survey of bioactivity evaluation, the obtained hardystonite (HT) powders were pressed and immersed in Kukobo solution (SBF)The results indicated that nano-struacture hadystonite powder with crystalline size is 40 nm. The apatite formation ability,bioactivity and good mechanical behavior make it a good candidate in bone implant materials and open new insights in biomedical engineering. The apatite formation ability,bioactivity and good mechanical behavior make it a good candidate in bone implant materials and open new insights in biomedical engineering. | ||
کلیدواژهها | ||
Hardystonite؛ Bioactivity؛ Hydroxyapatite؛ Nano-materials؛ SBF | ||