The Influence of the Nickel Content on Microstructure and Mechanical Properties of the Al-Mg Weld Metal

Journal of Environmental Friendly Materials

مقاله 7، دوره 1، شماره 2، آذر 2017، صفحه 41-44   

نوع مقاله: Original Article

نویسنده

F. Sharifi

Iranian Institute of Welding and Nondestructive Testing (IWNT), Tehran, Iran.

چکیده

In this investigation, the microstructure and mechanical properties of the Al 5058 weld metals have been studied in respect of Nickel content in the range of 0.5 to 4.5 percent. Samples were produced by automatic TIG welding process in Butt weld condition with different wire feeder speed rate of pure nickel filler metal. The optical metallography and EDX analysis result shows that by increasing of the nickel content in the weld metal, the grain size decreased and the volume fraction of the          inter-metallic compounds of Nickel rich phase was increased. The mechanical test results show that by increasing of the nickel content in the weld metal, the tensile and yield strength increased, whilst impact energy and elongation decreased.

کلیدواژه‌ها

Nickel؛ Al 5000 Series؛ Weld Metal؛ Microstructure؛ Mechanical Properties

مراجع

[1] J. Norrish: Advanced welding processes, Woodhead publishing limited, Cambridge, England, (2006).

[2] R. J. Davis: ASM Specialty Hand book, Aluminum and aluminum alloys, ASM International, USA, (2013).  

[3] C. E. Cross, D. L. Olson and S. Liu: Aluminum welding hand book, 2nd Edition, Dekker, New York, USA, 1(2015).

[4] S. Honma, K. Yasuda, Weld. Int., 18(2004), 450.

[5] P. B. Dickerson, B. Irving, Weld. J., 72(1992), 45.

[6] G. Mathers: The welding of aluminum and it’s alloys, Wood head publishing limited, Cambridge, England, (2002).

[7] H. Okamato: Alloys phase diagrams, ASM International, USA, (2002).

[8] K. Esterling: Introduction to physical metallurgy of welding, second edition, Butterworth and Heinemann, Oxford, England, (1992).

[9] S. A. David, J. M. Vitek, Int. Met. Rev., 8(1989), 213.

[10] H. Sabet, The International Institute of Welding Congress, IIWC, Iran, (2009).

[11] H. Sabet, Welding of Nonferrous Metals, IWNT Publication, Tehran, (2014).