Evaluation of thermal and antimicrobial behavior of Montmorillonite nanoclay modified with 2-Mercaptobenzothiazole | ||
Journal of Nanoanalysis | ||
مقاله 4، دوره 5، شماره 1، خرداد 2018، صفحه 26-35 اصل مقاله (935.75 K) | ||
نوع مقاله: Original Research Paper | ||
شناسه دیجیتال (DOI): 10.22034/jna.2018.541847 | ||
نویسندگان | ||
Milad Edraki1؛ Davood Zaarei* 2 | ||
1Polymer Department, Technical Faculty, South Tehran Branch, Islamic Azad University, Tehran, Iran | ||
2polymer department,technical faculty,south Tehran branch,Islamic Azad University,Tehran,Iran | ||
چکیده | ||
Thermal and antimicrobial properties of hybrid synthesized compounds were evaluated in the present study. Hybrid structures were synthesized via two main organic and inorganic components, namely: 2-Mercaptobenzothiazole (MBT) and sodium Montmorillonite clay (Na+- MMT). The synthesis process took place in a direct reaction, intercalation; and the resulting material was characterized. Results of scanning electron microscope (SEM), Energy dispersive X-ray spectroscopy (EDS), transmission electron microscope (TEM), and small-angle X-ray scattering (SAXS) and Fourier transform infrared spectroscopy (FTIR) confirmed MBT penetration of particles into the inner space of the clay layers and interaction between the two organic and inorganic phases. Also, thermal properties of the resulting compounds were evaluated by thermo gravimetric analysis (TGA) and differential thermalgravimetric (DTG). It was found that while MBT sample had relatively low degradation temperature (about 250°C), the MBT-modified clay compound showed superior thermal stability, and in high temperatures, less weight loss as compared to MBT. Antimicrobial properties of the hybrid nano compound against five types of bacteria, two types of fungus and one type of yeast were examined using well diffusion agar method and minimum inhibitory concentration (MIC). The diameter of inhibition zone was measured and their antimicrobial potential was compared with two common antibiotics: gentamicin and rifampin. The concentration of about 1000 μg/mL of MBT-MMT showed antibacterial performance equal to 250 μg/mL of rifampin. Also, 1000 μg/mL of this material was required to inhibit the growth of important bacteria. | ||
کلیدواژهها | ||
clay؛ layered silicate؛ Hybrid compounds؛ thermal stability؛ Antimicrobial properties | ||