An investigation on metallurgical and mechanical properties of vacuum brazed Ti-6Al-4V to 316L stainless steel using Zr-based filler metal

Journal of Advanced Materials and Processing

مقاله 7، دوره 1، شماره 1، فروردین 2013، صفحه 47-54   

نوع مقاله: Research Paper

نویسندگان

M.E Bajgholi¹؛ R Soltani Tashi^{* 2}؛ A.A Akbari Mousavi³؛ E Heshmat Dehkordi⁴

¹Department of Material Engineering, Science and Research Branch, Islamic Azad University, Tehran, Iran

²Department of Mechanical Engineering, Aliabad Katoul Branch, Islamic Azad University, Aliabad Katoul, Iran

³School of Metallurgy and Materials Engineering, College of Engineering, University of Tehran, Tehran, Iran

⁴Department of Engineering, Allameh University, Shahrekord, Iran

چکیده

Both Ti-6Al-4V and 316L stainless steels are widely used as engineering alloys. Fusion welding of these two alloys is not easily possible due to their incomplete solubility in each other. Brazing is one of the best choices for joining dissimilar alloys. In this study, wettability experiments were done at 940 and 970 ºC for 5, 15 and 30 min. Also, joining of these two alloys was carried out at 940 and 970 ºC for 15 min. Optical and scanning electron microscope (SEM) were used for metallurgical observations. Moreover, mechanical properties of the brazed joint were investigated using microhardness test. The results showed that some reaction layers were composed in the brazed joint’s cross section. Ni-Ti intermetallic compounds were also observed in the brazed joint. Investigation of mechanical properties showed that hardness in the joint’s center is higher than base metals.

کلیدواژه‌ها

Ti-6Al-4V؛ Stainless steel؛ Brazing؛ Zr-Based Braze Alloy