Chemical precipitation and characterization of multicomponent Perovskite Oxide nanoparticles – possible cathode materials for low temperature solid Oxide fuel cell

International Journal of Nano Dimension

مقاله 2، دوره 5، شماره 1، خرداد 2014، صفحه 1-10   

نوع مقاله: Reasearch Paper

شناسه دیجیتال (DOI): 10.7508/ijnd.2014.01.001

نویسندگان

Devi Radhika؛ A. Samson Nesaraj^*

Department of Chemistry, Karunya University, Coimbatore – 641 114, Tamil Nadu, India.

چکیده

A set of multicomponent perovskite oxide nanoparticles based on La_1-xSr_xCo_1-yFe_yO_3-δ(LSCF) were prepared by a simple chemical precipitation method for application in low temperature solid oxide fuel cells (LT-SOFC) as cathode materials.  The precursor materials used in this synthesis were lanthanum nitrate hexahydrate [La(NO₃)₃.6H₂O], strontium nitrate [Sr(NO₃)₂], cobalt nitrate hexahydrate [Co(NO₃)₂.6H₂O], ferric nitrate nonahydrate [Fe(NO₃)₃.9H₂O] [as basic materials] and sodium hydroxide [as precipitator material] and PVA [as surfactant]. Throughout the experiment, pH was maintained as pH > 9 by the addition of alkali (NaOH). A mixture of metal hydroxides (brown coloured) was formed when the aqueous mixture of basic materials mixed with the aqueous precipitant (NaOH) solution in proper stoichiometric compositions. The resultant hydroxide mixture was washed with ethanol and water mixture (1:9 volume %) to remove any unwanted impurities present along with the precipitate. The purified precipitate was dried at 50 – 100^oC and heat treated at 300^oC, 450^oC, 600^oC and 750^oC for 2 hours each to get phase pure composite oxide powder. The resultant powder was characterized with TGA / DTA, XRD, FT-IR, Particle Size analysis and SEM. From the results, it was found that the chemical precipitation can be used effectively to prepare phase pure multicomponent perovskite oxides for application in SOFCs.

کلیدواژه‌ها

Chemical precipitation؛ Multicomponent Perovskite Oxide nanoparticles؛ Cathode materials؛ SOFC