Study of multilayer and multi-component coatings deposited using cathodic Arc technique on H-13 hot work steel for die-casting applications

International Journal of Nano Dimension

مقاله 8، دوره 11، شماره 2، تیر 2020، صفحه 177-187   

نوع مقاله: Reasearch Paper

نویسندگان

Rajesh Mundotia^{* 1، 2}؛ Tatyarao Ghorude¹؛ Ashwin Kale²؛ Umesh Mhatre²

¹Department of Physics, N B Mehta Science College, Bordi, Palghar-401701, India.

²Surface Modification Technologies Pvt. Ltd, Vasai (East), Maharashtra: 401 208, India.

چکیده

Die casting process is used since long, but even today problems like erosion, corrosion, soldering and sticking affect die life. These dies undergo thermal cyclic loads from 70 ^oC to 600 ^oC during processing. Physical Vapor Deposition (PVD) hard coating can play an important role in such extreme applications. In the present work, we report the use of Chromium based multilayer CrN/Cr (M-CrN) coatings and multi-component aluminium titanium based AlTiN (M-AlTiN) coatings. The H-13 steel substrate samples were prepared using cathodic arc deposition technique. Structural properties of the coated samples were studied using XRD and SEM techniques. Tribological and mechanical properties of the coatings were studied using Calo-test and Micro-hardness test respectively. Potentiostat technique was used to study the effect of 1 M HCl solution on these coatings. Thermal fatigue (TF) test was conducted by heating the sample to around 600 ^oC and rapidly cooling it to room temperature imitating the die casting process conditions. After multiple cycles, it was observed that M-AlTiN coated samples outperform M-CrN coated samples in terms of wear, oxidation and adhesion properties. It was observed that formation of oxide layer on the coated surface during the thermal cycling inhibits further oxidation of the coating layer and result in enhanced productivity and efficiency of dies.

کلیدواژه‌ها

Coating Adhesion؛ Die Casting Application؛ H-13 Hot Work Steel؛ PVD Coatings؛ Thermal Fatigue؛ Wear Rate

مراجع

[1]     Kovacevic L., Terek P., Miletic A., Kukuruzovic D., Koric B., Panjan P., (2018), Industrial evaluation of duplex PVD hard coatings for HPDC. J. Braz. Soc. Mech. Sci. Eng. 40: 271-278.

[2]     Mitterer C., Holler F., Ustel F., Heim D., (2000), Application of hard coatings in aluminium die casting soldering, erosion and thermal fatigue behaviour. Surf. Coat. Technol. 125: 233–239.

[3]     Sundqvist M., Hogmark S., (1993), Effects of liquid aluminium on hot-work tool steel. Tribol. Int. 26, issue 2: 129-134.

[4]     Liu B., Wang B., Yang X., Zhao X., Qin M., Gu J., (2019), Thermal fatigue evaluation of AISI H13 steels surface modified by gas nitriding with pre- and post-shot peening. Appl. Surf. Sci. 483: 45–51.

[5]     Li G., Li X., Wu J., (1998), Study of the thermal fatigue crack initial life of H13 and H21 steels. J. Mater. Process. Technol. 74: 23–26.

[6]     Wang B., Zhao X., Li W., Qin M., Gu J., (2018), Effect of nitrided-layer microstructure control on wear behavior of AISI H13 hot work die steel. Appl. Surf. Sci. 431: 39-43.

[7]     Legg K. O., Graham M., Chang P., Rastagar F., Gonzales A., Sartwell B., (1996), The replacement of electroplating. Surf. Coat. Technol. 81: 99-105.

[8]     Paiva J. M., Fox-Rabinovich G., Locks Junior, E., Stolf P., Seid Ahmed Y., Matos Martins M., Bork C., Veldhuis S., (2018), Tribological and wear performance of nanocomposite PVD hard coatings deposited on aluminum die casting tool. Materials. 11: 358-363.

[9]     Peng J., Zhu Z., Su D., (2019), Sliding wear of nitrided and duplex coated H13 steel against aluminium alloy. Tribol. Int. 129: 232-238.

[10] Wang B., Bourne G. R., Korenyi-Both A. L., Monroe A. K., Midson S. P., Kaufman M. J., (2016), Method to evaluate the adhesion behavior of aluminum-based alloys on various materials and coatings for lube-free die casting. J. Mater. Process. Technol. 237: 386-393.

[11] Bobzin K., Brögelmann T., Brugnara R. H., Kruppe N. C., (2015), CrN/AlN and CrN/AlN/Al₂O₃ coatings deposited by pulsed cathodic arc for aluminum die casting applications. Surf. Coat. Technol. 284: 222-229.

[12] Fazlalipour F., Naghashnejan M., Nushari M. N., (2019), Evaluation of adhesion and erosion/corrosion resistance of Nano-composite and Nano-multilayer thin films in molten aluminum alloy. SN Appl. Sci. 1: 1308-1313.

[13] D'Avico L., Beltrami R., Lecis N., Trasatti S. P., (2019), Corrosion behavior and surface properties of PVD coatings for mold technology applications. Coatings. 9: 7-14.

[14] Okumiya M., Gripentrog M., (1999), Mechanical properties and tribological behavior of TiN–CrAlN and CrN–CrAlN multilayer coatings. Surf. Coat. Technol. 112: 123–128.

[15] Paldey S., Deevi S. C., (2003), Single layer and multilayer wear resistant coatings of (Ti,Al)N: A review. Mater. Sci. Eng: A. 342: 58-79.

[16] Wilczek A., Morgiel J., Rogal Ł., Maziarz W., Smolik J., (2020), Microstructure and wear of (CrN/CrAlN)/(CrAlN/VN) and (CrN/TiAlN)/(TiAlN/VN) coatings for molds used in high pressure casting of Aluminum. Coatings. 10: 261-272.

[17] Rutherford K. L., Hutchings I. M., (1996), A micro-abrasive wear test, with particular application to coated systems. Surf. Coat. Technol. 79: 231-239.

[18] Oliver W. C., Pharr G. M., (1992), An improved technique for determining hardness and elastic modulus using load and displacement sensing indentation experiments. J. Mater. Res. 7: 1564-1583.

[19] Mundotia R., Thorat N., Kale A., Mhatre U., Kothari D. C., Kovacs T., Ghorude T., (2019), Study of corrosion properties of CrN and multilayer CrN/Cr coating at different electrolyte temperatures deposited on stainless steel by vacuum arc process. AIP Conf. Proceed. 2115: 030313.

[20] Bull S. J., Berasetegui E. G., (2006), An overview of the potential of quantitative coating adhesion measurement by scratch testing. Tribol. Int. 39: 99–114.

[21] Vidakis N., Antoniadis A., Bilalis N., (2003), The VDI 3198 indentation test evaluation of a reliable qualitative control for layered compounds. J. Mater. Process. Technol. 143–144: 481–485.

[22] Abusuilik Saleh B., (2015), Pre-intermediate, and post-treatment of hard coatings to improve their performance for forming and cutting tools. Surf. Coat. Technol. 284: 384-395.

[23] Schönjahn C., Ehiasarian A. P., Lewis D. B., New R., Münz W.-D., Twesten R. D., Petrov I., (2001), Optimization of in situ substrate surface treatment in a cathodic arc plasma: A study by TEM and plasma diagnostics. J. Vac. Sci. Technol. A. 19: 1415-1420.

[24] Thorat N., Mundotia R., Varma R., Kale A., Mhatre U., Patel N., (2018), Structural & oxidation behavior of TiN & Al_xTi_1-xN coatings deposited by CA-PVD technique. AIP Conf. Proceed. 1942: 080041.

[25] Chim Y. C., Ding X. Z., Zeng X. T., Zhang S., (2009), Oxidation resistance of TiN, CrN, TiAlN and CrAlN coatings deposited by lateral rotating cathode arc. Thin Solid Films. 517: 4845–4849.

[26] Conde A., Cristóbal A. B., Fuentes G., Tate T., Damborenea J. De., (2006), Surface analysis of electrochemically stripped CrN coatings. Surf. Coat. Technol. 201: 3588–3595.

[27] Wu Z. T., Qi Z. B., Zhu F. P., Liu B., Wang Z. C., (2013), Influences of Y addition on mechanical properties and oxidation resistance of CrN coating. Phys. Proced. 50: 150 – 155.

[28] Barshilia H. C., Jain A., Rajam K. S., (2004), Structure, hardness and thermal stability of nanolayered TiN/CrN multilayer coatings. Vacuum. 72: 241–248.

[29] Brooks J. S., Davidson J. L., Forder S. D., Munz W. D., Larsson M., (1997), A Mossbauer spectroscopy study of Ti–Fe interfaces produced by the PVD process. Thin Solid Films. 308–309: 351–357.