The Effect of Power, Maximum Cutting Speed and Specific Point Energy on the Material Removal Rate and Cutting Volume Efficiency in CO2 Laser Cutting of Polyamide Sheets

Journal of Modern Processes in Manufacturing and Production

دوره 9، شماره 3، آبان 2020، صفحه 23-39   

نوع مقاله: Research Paper

نویسندگان

Majid Hashemzadeh^* ؛ Reza Poorshaban

Department of Mechanical Engineering, Najafabad Branch, Islamic Azad University, Najafabad, Iran

چکیده

Material removal rate (MRR) and cutting volume efficiency (α_Vol) in laser cutting of commercial polyamide (Nylon) sheets have been studied in this research. A CO₂ laser cutting machine with the power of 100 W was used to cut polyamide (PA) sheets with thicknesses of 2 to 8 mm. The beam spot size on the upper surface of the sheet was 0.1 mm. The maximum cutting speeds for a variety of powers and thicknesses were specified under the same other laser cutting parameters. The specific point energy (Esp) was calculated for every combination of maximum cutting speed and power. Results show that for a given power, the maximum cutting speed exponentially decreases with increasing sheet thickness. The MRR increases logarithmically with power and for a given power, it rises as the sheet thickness decreases. The α_Vol increases with power until it reaches the apex of efficiency, then it slightly reduces with increasing power. Overall, the α_Vol decreases with increasing sheet thickness and Esp.

کلیدواژه‌ها

CO2 laser cutting؛ Polyamide (PA)؛ Material removal rate؛ kerf width

مراجع

[1] Petring, D., Schneider, F., Wolf, N. and Nazery, N. 2008. The relevance of brightness for high power laser cutting and welding. 27th International Congress on Applications of Lasers & Electro Optics (ICALEO): 95-103.

[2] Mahrle, A., Lutke, M. and Beyer, E. 2010. Fibre laser cutting: beam absorption characteristics and gas-free remote cutting. Proceedings of the Institution of Mechanical Engineers. Part C-Journal of Mechanical Engineering Science. 224 (C5): 1007-1018.

[3] Hashemzadeh, M., 2014. Investigation into fibre laser cutting. The University of Nottingham. PhD thesis.

[4] Riveiro, A., Quintero, F., Lusquiños, F., del Val, J., Comesaña, R., Boutinguiza, M. and Pou, J. 2012. Experimental study on the CO₂ laser cutting of carbon fiber reinforced plastic composite. Composites Part A: Applied Science and Manufacturing. 43(8): 1400-1409.

[5] Caiazzo, F., Curcio, F., Daurelio, G. and Minutolo, F. M. C. 2005. Laser cutting of different polymeric plastics (PE, PP and PC) by a CO₂ laser beam, J. Mater. Process. Technol. 159(3): 279-285.

[6] Powell, J., Al-Mashikhi, S.O., Kaplan, A.F.H. and Voisey, K.T. 2011. Fibre laser cutting of thin section mild steel: An explanation of the striation free effect. Optics and Lasers in Engineering. 49:1069-75.

[7] Hirano, K. and Fabbro, R. 2011. Experimental observation of hydrodynamics of melt layer and striation generation during laser cutting of steel. Physics Procedia. 12(Part A):555-64.

[8] Steen, W.M. 2005. Laser Material Processing, third edition: Springer.

[9] Hashemzadeh, M., Suder, W., Williams, S., Powell, J., Kaplan, A.F.H. and Voisey, K.T. 2014. The Application of Specific Point Energy Analysis to Laser Cutting with 1μm Laser Radiation. Physics Procedia. 56: 909-918

[10] Powell J. 1998. CO₂ laser cutting, Second edition, Springer, London.

[11] Haddadi, E., Moradi, M., Karimzad Ghavidel, A., Karimzad Ghavidel, A. and Meiabadi, S. 2019. Experimental and Parametric Evaluation of Cut Quality Characteristics in CO₂ Laser Cutting of Polystyrene. Optik. 184:103-114.

[12] Zhaia, Zh.,Wang, F. and Duan, H. 2019. Experimental study on 800 nm femtosecond laser cutting of polyamide in air. 194:163080.

[13] Riveiro, A., Quintero, F., Lusquiños, F., del Val, J., Comesaña, R., Boutinguiza, M. and Pou, J. 2012. Experimental study on the CO₂ laser cutting of carbon fiber reinforced plastic composite. Composites Part A: Applied Science and Manufacturing. 43(8), 1400–1409.

[14] Davari, M. and Hashemzadeh, M. 2018. The effect of bronze particles on CO₂ laser cutting of reinforced polytetrafluoroethylene. Int J Adv Manuf Technol. 96:4029–4039.

[15] Moradi, M., Mehrabi, O., Azdast, T. and Benyounis, K.Y. 2017. Enhancement of low power CO₂ laser cutting process for injection molded polycarbonate. Optics & Laser Technology. 96:208–218.

[16] Moradi, M., Mehrabi, O., Azdast, T. and Benyounis, K.Y. 2017. The effect of low power CO₂ laser cutting process parameters on polycarbonate cut quality produced by injection molding. Modares Mechanical Engineering. 17(2):93-100.

[17] Banerjee, S. S. and Bhowmick, A. K. 2015. Experimental study on the CO₂ laser cutting of novel polyamide 6/fluoroelastomer thermoplastic elastomeric blends. Rubber Chemistry and Technology. 88(1):125-137.

[18] DeIorio, I., DiIlio, A. and Tagliaferri, V. 1987. Cut edge quality of GFRP by pulsed lasermaterial interaction analysis. Proceedings of LAMP, high Temperature Society of Japan. 279-284.

[19] Brydson, J. A. 1989. Plastic Materials, Fifth edition. Butterworth.

[20] Campo, E. A. 2006. The Complete Part Design Handbook for Injection Molding of Thermoplastics, Hanser.

[21] Schwartz, S. S. and Goodman, S. H. 1982. Plastic Materials and Processes, Van Norstrand Retnhold.

[22] Beyler, C.L. and Hirschler, M.M. 2002 Thermal Decomposition of Polymers. SFPE Handbook of Fire Protection Engineering, Chapter 7: 111-131.

[23] Hashemzadeh, M. and Mohammadi, M. 2020. The Effect of Power and Maximum Cutting Speed on the Material Removal Rate and Cutting Volume Efficiency in CO2 Laser Cutting of Polycarbonate Sheets. Journal of Modern Processes in Manufacturing and Production. 9(1):5-23.