Evaluation of Optimal Conditions, Microstructure, and Mechanical Properties of Aluminum to Copper Joints Welded by FSW

Journal of Modern Processes in Manufacturing and Production

مقاله 6، دوره 9، شماره 4، بهمن 2020، صفحه 61-81   

نوع مقاله: Research Paper

نویسندگان

Ahmad Afsari^{* 1}؛ Shahin Heidari²؛ Jaleel Jafari¹

¹Department of Mechanical Engineering, Shiraz Branch, Islamic Azad University, Shiraz, Iran

²Bone and Joint Diseases Research Center, Shiraz University of Medical Sciences, Shiraz, Iran, P. O. Box: 71348-14336

چکیده

The joining of dissimilar metals by Friction stir welding (FSW) is one of the newest metal joining processes. In this research, the tool was made from H13 hot working steel, which has a concave shoulder with a 3-degree inclined angle. The welding operation performed using a milling machine. The non-homogeneous workpieces joining of the Al alloy (5083) and a sheet of annealed copper (ASTM B36) with a thickness of 2 mm was investigated by the FSW method.  The joining process was carried out at three tool transverse speeds of 25, 35, and 45 mm per minute and three rotational velocities of 1000, 1300, and 1600 rpm. Microstructural changes of the welded samples were analyzed by optical microscopy and scanning electron microscopy used to distinguish the type of phases. While its mechanical properties analyze according to different parameters used in the experiments. Also, the welded parts were subjected to microhardness and tensile tests. It found that the welding sample with a tool rotational speed of 1,300 rpm and a forward speed of 35 mm/min has the best mechanical properties, with a tensile strength of 82% and a yield strength of 80% of aluminum base metal. While welded components with a forward speed of 25 mm/min have tunnel defects and brittle phases of AlCu and Al2Cu formed in the stir region so that with the increase of rotational speed and forward speeds, the percentage of these brittle phases increases.

کلیدواژه‌ها

Non-homogeneous Metals؛ Friction Stir Welding (FSW)؛ Aluminum Series 5xxx؛ Copper Alloy ASTM B36؛ Mechanical Properties

مراجع

[1] Esmaeili, A., Givi, M.B. and Rajani, H.Z. 2011. A metallurgical and mechanical study on dissimilar Friction Stir welding of aluminum 1050 to brass (CuZn30). Materials Science and Engineering: A. 528(22-23):7093-7102.

[2] ASM International Handbook Committee. 1992. Properties and selection: nonferrous alloys and special-purpose materials. ASM International. 2:1143-1144.

[3] Pietrzyk, M., Cser, L. and Lenard, J.G. 1999. Mathematical and physical simulation of the properties of hot rolled products. Elsevier.

[4] Xue, P., Ni, D.R., Wang, D., Xiao, B.L. and Ma, Z.Y. 2011. Effect of friction stir welding parameters on the microstructure and mechanical properties of the dissimilar Al–Cu joints. Materials Science and Engineering: A. 528(13-14):4683-4689.

[5] Zum FÜgen, E., Von Halbzeugen, A., Pour, S. and La Jonction, D. 2005. Friction stir welding—innovative technology for joining aluminium components. Otto Graf Journal. 16:185-97.

[6] Saeid, T., Abdollah-Zadeh, A. and Sazgari, B., 2010. Weldability and mechanical properties of dissimilar aluminum–copper lap joints made by friction stir welding. Journal of Alloys and Compounds. 490(1-2):652-655.

[7] Mahoney, M.W., Rhodes, C.G., Flintoff, J.G., Bingel, W.H. and Spurling, R.A. 1998. Properties of friction-stir-welded 7075 T651 aluminum. Metallurgical and Materials Transactions A. 29(7):1955-1964.

[8] Otegui, J.L. and Fazzini, P.G. 2004. Failure analysis of tube–tubesheet welds in cracked gas heat exchangers. Engineering Failure Analysis. 11(6):903-913.

[9] Liu, H.J., Shen, J.J., Xie, S., Huang, Y.X., Cui, F., Liu, C. and Kuang, L.Y. 2012. Weld appearance and microstructural characteristics of friction stir butt barrier welded joints of aluminium alloy to copper. Science and Technology of Welding and Joining. 17(2):104-110.

[10] Bhamji, I., Moat, R.J., Preuss, M., Threadgill, P.L., Addison, A.C. and Peel, M.J. 2012. Linear friction welding of aluminium to copper. Science and Technology of Welding and Joining. 17(4):314-320.

[11] Esmaeili, A., Rajani, H.Z., Sharbati, M., Givi, M.B. and Shamanian, M. 2011. The role of rotation speed on intermetallic compounds formation and mechanical behavior of friction stir welded brass/aluminum 1050 couple. Intermetallics. 19(11):1711-1719.

 [12] Shojaeefard, M.H., Akbari, M., Khalkhali, A., Asadi, P. and Parivar, A.H. 2014. Optimization of microstructural and mechanical properties of friction stir welding using the cellular automaton and Taguchi method. Materials & Design. 64: 660-666.

[13] Beygi, R., Kazeminezhad, M. and Kokabi, A.H. 2012. Butt joining of Al–Cu bilayer sheet through friction stir welding. Transactions of Nonferrous Metals Society of China. 22(12): 2925-2929.

[14] Bisadi, H., Tavakoli, A., Sangsaraki, M.T. and Sangsaraki, K.T. 2013. The influences of rotational and welding speeds on microstructures and mechanical properties of friction stir welded Al5083 and commercially pure copper sheets lap joints. Materials & Design. 43: 80-88.