اخبار و اعلانات

 آمار

تعداد نشریات418
تعداد شماره‌ها10,005
تعداد مقالات83,621
تعداد مشاهده مقاله78,331,671
تعداد دریافت فایل اصل مقاله55,377,884
Maiti, Madhuchhanda, Basak, Ganesh C., Srivastava, Vivek K., Jasra, Raksh Vir. (1396). Influence of synthesized nano-ZnO on cure and physico-mechanical properties of SBR/BR blends. نشریه علمی پژوهشی دانشگاه آزاد اسلامی, 8(3), 273-283. doi: https://doi.org/10.1007/s40090-016-0107-7
Madhuchhanda Maiti; Ganesh C. Basak; Vivek K. Srivastava; Raksh Vir Jasra. "Influence of synthesized nano-ZnO on cure and physico-mechanical properties of SBR/BR blends". نشریه علمی پژوهشی دانشگاه آزاد اسلامی, 8, 3, 1396, 273-283. doi: https://doi.org/10.1007/s40090-016-0107-7
Maiti, Madhuchhanda, Basak, Ganesh C., Srivastava, Vivek K., Jasra, Raksh Vir. (1396). 'Influence of synthesized nano-ZnO on cure and physico-mechanical properties of SBR/BR blends', نشریه علمی پژوهشی دانشگاه آزاد اسلامی, 8(3), pp. 273-283. doi: https://doi.org/10.1007/s40090-016-0107-7
Maiti, Madhuchhanda, Basak, Ganesh C., Srivastava, Vivek K., Jasra, Raksh Vir. Influence of synthesized nano-ZnO on cure and physico-mechanical properties of SBR/BR blends. نشریه علمی پژوهشی دانشگاه آزاد اسلامی, 1396; 8(3): 273-283. doi: https://doi.org/10.1007/s40090-016-0107-7

Influence of synthesized nano-ZnO on cure and physico-mechanical properties of SBR/BR blends

International Journal of Industrial Chemistry
دوره 8، شماره 3، آذر 2017، صفحه 273-283
نوع مقاله: research article
شناسه دیجیتال (DOI): https://doi.org/10.1007/s40090-016-0107-7
نویسندگان
Madhuchhanda Maiti؛ Ganesh C. Basak* ؛ Vivek K. Srivastava؛ Raksh Vir Jasra
Reliance Technology Group, Vadodara Manufacturing Division, Reliance Industries Ltd., Vadodara, Gujarat, 391346, India
چکیده
This study focuses on the synthesis of zinc oxide (ZnO) nanoparticles by high temperature calcination as well as low-temperature hydrolysis methods and their efficiency as cure activator in styrene-butadiene rubber/polybutadiene rubber blend. The synthesized nano-ZnO samples were characterized by means of X-ray diffraction, BET surface area and transmission electron microscopy. The synthesized nano-ZnO samples had wurtzite structure and average particle size in the ‘nm’ range. ZnO nanoparticles, synthesized on sepiolite template, were of smallest particle size (maximum number of particles in the range of 7–12 nm) and highest surface area (104 m2g−1). Polyethylene glycol (PEG)-6000 coated ZnO nanoparticles had rod-like structure; average diameter of the rods was 50 nm. In the case of PEG-coated ZnO containing compounds, optimum cure time of the blend was decreased by 5 min compared to that of standard rubber grade-ZnO containing compound (used as reference). Optimum cure time was lowered by 7–10 min in the case of synthesized nano-ZnO containing compounds compared to the reference ZnO based compound in presence of conventional filler, carbon black. It was also observed from ICP-OES analysis that the presence of very little amount of magnesium in one of the synthesized ZnO has noticeable impact on cure properties. PEG-coated ZnO increased the tensile strength of gum vulcanizates by 28% compared to the reference ZnO, acting as nanofiller at 3 phr loading. The study of curing behavior in dynamic condition was carried out using DSC. The results differ slightly from static curing except PEG modified nano-ZnO. Use of ZnO nanoparticles could provide faster crosslinking, better reinforcement at lower concentration compared to reference ZnO.
کلیدواژه‌ها
Nano-ZnO؛ SBR؛ BR؛ Curing؛ Cure properties