Effect of Heat Treatment on the Intermetallic Compounds and Mechanical Properties of Explosive Weld Interface of three Al 5083, Al 1050 and St 1515 Layers

Journal of Environmental Friendly Materials

مقاله 3، دوره 4، شماره 2 - شماره پیاپی 8، اسفند 2020، صفحه 9-19   

نوع مقاله: Original Article

نویسندگان

Bakhtiari H¹؛ Mokhtariniya F²؛ Khanzadeh M. R³؛ Farvizi M¹

¹Institute of Materials and Energy, Meshkin Dasht, Iran

²Faculty of Materials Engineering, Bandarabbas Branch, Islamic Azad University, Bandarabbas, Iran

³Center for Advanced Engineering Research, Majlesi Branch, Islamic Azad University, Isfahan, Iran

چکیده

In this research, the effect of heat treatment on the microstructure and mechanical properties of intermetallic compounds of welding joint interface of three explosive layers of 5083 and 1050 aluminum as flying and intermediary plates and AISI steel sheet as the base plate has been discussed and investigated. To show the effect of temperature and time, the welded samples with stand-off distance of 6, 8, and 10mm and the explosive load of 2.41 were placed on heat treatment in the constant temperature of 315°C and 450°C within a furnace protected by Argon gas for six hours. Laboratory investigations have been conducted by the use of photomicroscope, scanning electronic microscopy, and microhardness assessing tests. Metal compounds of the interface were specified by the use of EDS analysis. In the considered samples before heat treatments, the interface of the joint has been converted from the short wavy state into the vertical wavy state by the increase of stand-off distance from 6 mm to 10 mm, and the average diameter of intermetallic layers has been increased in a range from 0.1±1.89 micrometer to 0.07± 3.13 micrometer as well. Also, microhardness has been decreased by the increase of intermetallic compounds from 266 Vickers in the sample with a stand-off distance of 10 mm to 205 Vickers in the sample with a stand-off distance of 8mm in the steel section. The performance of treatment in temperatures of 315°C and 450°C for six hours has been led to increasing the diameter of the intermetallic compounds layer.

کلیدواژه‌ها

Heat Treatment؛ Explosive Welding؛ Intermetallic Compounds؛ Stand-off Distance؛ Microhardness

مراجع

[1] S. Saravanan and K. Raghukandan, Mater. Manuf. Process., 28 (2013), 589.

[2] A. Durgutlu, H. Okuyucu and B. Gulenc, Mater. Des., 29, (2008), 1480.

[3] A. Patterson, Fundamentals of Explosion Welding, ASM Handbook, Vol 6 Welding, Brazing, and Soldering, ASM International, USA, (1993) 160-164.

[4] B. S. Zlobin, Combustion, Explosion, and Shock Waves., 38 (2002), 374.

[5] R. Kacar and M. Acarer, Mater. Process. Technol., 153 (2009), 91.

[6] A. Nobili: Explosion bonding process, Risvsaltes plant, France.

[7] L. Tricarico, R. Spina, D. Sorgente and M. Brandizzi , Mater. Des., 30 (2009), 2693.

[8] G. Temizel and M. Ozenbas, Turkish J. Eng. Env., (2007), 71.

[9] S. Phengsakul and A. Rodchanarowan, Energy Procedia., 34 (2013), 782.

[10] G. Tem Izel, Turkish J. Eng. Env. Sci., 31 (2007), 71.

[11] B. S. Zlobin, Mater. Des., 24 (2003), 617.

[12] S. A. A. Akbari Mousavi and P. Farhadi Sartangi , Mater. Sci. Eng., A., 494 (2008), 329.

[13] F. Findik, R. Yilmaz, and T. Somyurek, Sci. Res. Essays. 8 September., 19 (2001), 4141.

[14] J. Lokaj and M. Benak, Metal., 5, (2010), 18.

[15] J. Banker, Draft of Paper for presentation TMS 131st Annual Meeting., (2002).

[16] M. R. Khanzadeh Gharah Shiran1, H. Bakhtiari, M. J. Ghadami and H. Nazemi, J. Energetic Mater., 12, (2017), 207.

[17] Standard test method for tension shear. ASTM D 3165-95, Philadelphia, (2012).

[18] s. Jun, T. Jie and G. Zhong, Trans. Nonferrous Met. Soc. China., (2011), 2175.

[19] Standard Test Method forVickers Hardness of Mater. ASTM E384-11, Philadelphia, (2012).

[20] N. Kahraman and B. Gulence, J Mater. Process. Tech. , 169 (2005) , 67.

[21] I. Samardzic, B. Matesa and I. Kladaric, Metabk. , 50 (2011) , 159.

[22] M. Benak, M. Turna, M. Ozvold, P. Nesvadba, J. Lokaj, L. Caplovic, F. Kovac and V. Stoyka , Roznov pod Radhostem Czech Republic 18 , (2010).

[23] M. Potesser and T. Schoeberl, The Minerals. Metals  Mater. Society., (2006).

[24] Z. Blazynski, forming and compaction, Appl. Sci. 1Publishers, (1983).

[25] M. Acarer, B. Gulenc and F. Findik, Mater. Des. , 24 (2003) , 659.

[26] L. Tricarico and R. Spina , Arch. Mater. Sci. Eng., 37 (2009) , 85.

[27] H. Danesh Manesh and A. Karimi Taheri, Mater. Des., 24 (2003) , 617.

[28] N. Kengkla and N. Tareelap , 1st Mae Fah Luang University Int. Conf., (2012).